The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) Après ajustement à haute température et traitement cryogénique, la solution est d'abord chauffée à 950 degrés pendant 90 minutes. En raison de l'augmentation du point Ms, une petite quantité de martensite peut être obtenue par refroidissement à température ambiante ; quantité de martensite.
(3) Après le traitement en solution par la méthode de déformation à froid, la déformation à froid est effectuée à température ambiante. La quantité de martensite formée dans le tube sans soudure 904L lors de la déformation à froid est liée à la quantité de déformation et à la composition du tube en acier inoxydable 904L.
Les trois méthodes ci-dessus sont des méthodes couramment utilisées pour le traitement en solution des tuyaux en acier inoxydable. J'espère qu'ils pourront vous aider.